Pengaruh Bioconc Expired Dalam Kuat Tekan Beton

Arifien Nursandah, Faizah Rizki Jannah

Abstract

The method used in this research is the method of the Department of Environment (DOE) which is usually referred to the design of the English manner stipulated in SNI 03-2834-2000 namely "Procedure for Making Plans Mixed Concrete Normal". Making concrete mix Bioconc in this study as many as 36 pieces with aged care 7, 14, 21 and 28 days and testing materials in the form slinder 30 x 15 cm with a variation of normal concrete without mix and concrete with the addition of additives Bioconc ie 20% and 30% of the sheer number of cement. Quality of the concrete is planned fc '30 MPa. The results of the study with normal concrete compressive strength of the resulting 24.94 MPa, using additives Bioconc 20% of the compressive strength of the resulting 24.63 MPa, using a 30% Bioconc compressive strength of 19.94 MPa produced using additives as an additive in mixed concrete gives concrete strength decreased from normal concrete mix. It is advisable to pay attention to several factors such as the mix design especially for the concrete mix additives, Cement Water Factor (FAS), material testing, concrete casting and solidification.

References

ASTM C 117 - 03. Standard Test Method for Materials Finer than 75-μm (No. 200) Sieve in Mineral Aggregates by Washing. United States: ASTM International, 2003.

ASTM C 127 - 01. Standard Test Method for Density, Relative Density (Specific Gravity), and Absorption of Coarse Aggregate. United States: ASTM International, 2001.

ASTM C 128 - 01. Standard Test Method for Density, Relative Density (Specific Gravity), and Absorption of Fine Aggregate. United States: ASTM International, 2001.

ASTM C 136 - 96. Standard Test Method for Sieve Analysis of Fine and Coarse Aggregates. United States: ASTM International, 1996.

ASTM C 143 - 03. Standard Test Method for Slump of Hydraulic-Cement Concrete. United States: ASTM International, 2003.

ASTM C 1437 - 01. Standard Test Method for Flow of Hydraulic Cement Mortar. United States: ASTM International, 2001.

ASTM C 150 - 02. Standard Specification for Portland Cement. United States: ASTM International, 2002.

ASTM C 187 - 98. Standard Test Method for Normal Consistency of Hydraulic Cement. United States: ASTM International, 1998.

ASTM C 188 - 95. Standard Test Method for Density of Hydraulic Cement. United States: ASTM International, 1995.

ASTM C 40 - 04. Standard Test Method for Organic Impurities in Fine Aggregates for Concrete. United States: ASTM International, 2004.

ASTM C 496 - 04. Standard Test Method for Splitting Tensile Strength of Cylindrical Concrete Specimens. United States: ASTM International, 2004.

ASTM C 566 - 97. Standard Test Method for Total Evaporable Moisture Content of Aggregate by Drying. United States: ASTM International, 1997.

Anas, Azwar, pembimbing : DR.Eng Januarti Jaya Ekaputri, ST, M Eng dan Prof. DR. Ir. Triwulan, DEA, Thesis tentang "Pemanfaatan Mikrobakteri pada Beton Mutu Tinggi dengan Tambahan Silica Fume", Juni -2015

Masoud Ghandehari. “Comparison of Compressive and Splitting Tensile Strength of High-Strength Concrete With and Without Polypropylene Fiber Sheated to High Temperatures.” Fire Safety Journal 44, 2009: 1015-1022.


DOI: http://dx.doi.org/10.30651/ag.v2i1.616
DOI (PDF (Bahasa Indonesia)): http://dx.doi.org/10.30651/ag.v2i1.616.g439

Refbacks

  • There are currently no refbacks.